Treatment Agent Of Zinc And Galvanized Steel
Treatment procedure
 |
|
Computer crust
|
Degreasing powder & agent
|
CF NO.
|
Using method
|
Characteristic
|
||
|
|
Concentration(%)
|
Temperature(°C)
|
Time(min)
|
|
|
103
|
3~5
|
Normal temperature~50 |
3~5
|
It is used for general degreasing and immersion. |
|
105C
|
1~2
|
Normal temperature~50 |
3~5
|
It is a degreasing and adding agent and restrain peek agent and is used for immersion. |
|
171A
|
3~5
|
Normal temperature~50 |
3~5
|
It is used for general degreasing and immersion with weak alkaline. |
|
130
|
2
|
Normal temperature~50 |
1.5~2.5
|
It is used for general degreasing and spraying. |
|
137
|
2
|
Normal temperature~50 |
1.5~2.5
|
It is used for general degreasing and spraying. |
Surface adjustment
|
CF NO.
|
Using method
|
Characteristic
|
||
|
|
Concentration(%)
|
Temperature(°C)
|
Time(min)
|
|
|
BK-3
|
0.2
|
Normal temperature |
0.5~1
|
It can increase the reaction of coated film for fine crystal. |
|
BK-3A
|
0.2
|
Normal temperature |
0.5~1
|
It can increase the reaction of coated film for fine crystal. |
Filming agent
|
CF NO.
|
Using method
|
Characteristic
|
||
|
|
Concentration(%)
|
Temperature(°C)
|
Time(min)
|
|
|
401A
|
6~8
|
Normal temperature~45 |
2~5
|
It is suitable for immersion with cycling method and is used for galvanized steel. |
|
401B
|
6~10
|
Normal temperature~45 |
2~5
|
It is suitable for immersion with cycling method and is used for galvanized steel. |
|
407
|
5
|
40~50
|
2~5
|
It is suitable for immersion with cycling method and has good corrosion resistance during coated film formation. |
|
407A
|
5~7
|
40~50 |
2~5
|
It is suitable for immersion with cycling method and has good corrosion resistance during coated film formation. |
|
407NA
|
2.5~4
|
Normal temperature~50 |
1.5~3
|
It is suitable for spraying and is used for galvanized steel. |
|
707NB
|
2.5~4
|
Normal temperature~50
|
1.5~3
|
It is suitable for spraying and is used for galvanized steel. |
|
407S
|
4
|
45~50 |
1.5~3
|
It is suitable for spraying and has good corrosion resistance during coated film formation. |
|
407SA
|
4~5
|
45~50 |
1.5~3
|
It is suitable for spraying and has good corrosion resistance during coated film formation. |
|
555N
|
2~3
|
40~60
|
1.5~3
|
It is a coated film with good corrosion resistance, thin film, fine and density. |
|
Z35
|
A20, B20CC
|
20~40 |
10″~30″
|
It is an olive and green coated film with zinc and steel plate |
|
700
|
0.8~1
|
Normal temperature~50 |
15″~1
|
It is suitable for powder of high class and it can increase the coated film of corrosion resistance on liquid coating. |
|
5101
|
3.5
|
45~50
|
1.5~3
|
It is suitable for zinc phosphate coated film with sprayingU+00A0 and it has good corrosion resistance. |
 |
 |
|
Engine cover |
Door plate of auto
|
 |
 |
|
Auto plate |
ED engine cover
|
 |
 |
|
Auto parts
|
ED auto plate
|